1.4441 IMPLANT GRADE

~316LVM 

Chemical Composition Limits

Weight % Si  Mn P S Cr  Mo Ni 

 1.4441

IMPLANT GRADE

 0.03

max

 1.00

max

 2.00

max

0.025

max

0.010

max

17.0-19.0  2.50-3.20  13.0-15.5  0.10

max

Other Chemically similar Specifications 

Weight %  C  Si Mn P S Cr Mo Ni N
 AFNOR 

X2CrNiMo 18-15-3

 0.03

max

1.00

max

 2.00

max

0.025

max

0.010

max

17.0-19.0   2.50-3.20  13.0-15.5 0.10

max

 

Stainless Steel Rod, Bar, Wire, Cold drawn, ground and polished

Standard length of bars: 2 or 3 mtr.

Austenitic Stainless Steel for implants, with high corrosion resistance.

According to ISO 5832/1, F-138 Vacuum melt grade (VAR)

For surgical instruments, fracture fixation devices, screws for implants and many more similar applications.

 

Material

Features:

Type 316L is an improved corrosion resistant Chrome-Nickel steel alloy with a high content of Molybdenum. The material is non-magnetic, even after several cold forming operations.

It is not a typical freemachining grade and therefore not recommended for difficult high speed machining

Tolerance

Standard ISO h8 (up to +/- 0.002mm tolerance available on short delivery)