Chronifer Labor 13% material is
Manufactured in Rod, Bar and coil
AISI 416 Stainless Steel, WS 1.4005
Resists to water and stream corrosion after tempering
and a forced polishing of the parts. For optimum corrosion
resistance, surfaces must be free of scale and foreign particles and
finished parts should be passivated. Condition T is pre-tempered to 26-32
HRC.
Diameters
Ø< 2.00 mm: cold drawn and polished
Ø>= 2.00mm: cold drawn, ground and
polished. Surface roughness N6-N7
Availability
In bars, standard length 3m (2m) and in coil
Tolerances
h8 more accurate tolerances on request
Mechanical properties
Tensile strength at delivery form 650-850 N/mm 2
After annealing 500-700 N/mm 2
Heat Treatment
Hardening in oil 950 to 1000 ºC, content of carbon
must be above 0.9%
tempering 600-700 ºC
Maximum hardness 43 HRC
Cutting rate
40 to 65 m/mm depending on the lubrication oil, the
cutting tool,
the shape of parts etc.
Standard Stock
most current dimensions from 0.80 to 13m round
(English sizes 1/4", 1/8")
|