Chromium Stainless Steel with 17% Cr

Chemical Composition Limits

Weight %  C Si Mn P S Cr Mo Fe

CHRONIFER 

LABOR 17%

 0.10-0.17 max 1.00  max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 

Other Chemically similar Specifications 

Weight %  C Si Mn P S Cr Mo Fe
WS 1.4104  0.10-0.17 max 1.00   max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 
DIN X 12 CrMoS 17  0.10-0.17 max 1.00   max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 
AISI 430F  0.10-0.17 max 1.00   max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 
AFNOR Z 13 CF 17  0.10-0.17 max 1.00   max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 
EN X 14 CrMoS 17  0.10-0.17 max 1.00   max 1.50  max 0.06  0.15-0.35  15.50-17.50 0.20-0.30 Rem 

CHRONIFER LABOR 17%

Chromium Stainless Steel with 17% Cr

AISI 430F Stainless Steel WS 1.4104

This half ferritic free cutting stainless steel resists to water and steam corrosion and also mild alkalinity media.

 

Availability

Coils: cold drawn +polished; 10-35kg/coil

Bars Ø 0-1.99mm: cold drawn and polished

Bars Ø 2.00-40mm cold drawn, ground and polished

Bar lengths 2m or 3m Surface roughness N5-N6

 

Standard Tolerances

Diameter h7, h8 (4.00, 6.00 and 10.00 in tol h6)

Out of roundness/eccentricity: 1/2 of dia tolerance

Tolerance in length 30mm

 

Heat Treatment

Soft annealing 800-850 ºC

slow furnace cooling (2-4 hours)

Hardening: 1000-1050 ºC

Max obtainable hardness:40 HRC

 

Cutting rate

50-60m/min (approximate value, depending on the lubrication oil, the cutting tools, the shape of parts)

 

Stock Range

Ø 1.00 to 30.00mm round full bars (1.60mm in coil) in stock, other dimension available on request.

 

 