Hardenable alloyed free cutting stainless steel

Chemical Composition Limits

Weight %  C Si Mn Cr Mo Fe
CHRONIFER LABOR M-13 0.40-0.50  1.60 max 1.00 max  12.50-14.50  max 0.20  max 0.60 Rem 

Other Chemically similar Specifications 

Weight %  C Si Mn Cr Mo Fe
WS 1.4034+s 0.40-0.50   1.60 max 1.00 max  12.50-14.50  max 0.20  max 0.60 Rem 
DIN X 46 CrS 13 0.40-0.50   1.60 max 1.00 max  12.50-14.50  max 0.20  max 0.60 Rem 
AISI 420F~ 0.40-0.50   1.60 max 1.00 max  12.50-14.50  max 0.20  max 0.60 Rem 

Chronifer Labor M-13 material is Manufactured in Rod, Bar and coil

AISI 420F ~ Stainless Steel

 

Material Properties

This product is a compromise between good machinability (S-Content), high wear resistance (Cr-content) and possibility for hardening (C-Content.  Chronifer Labor M 13 resists to corrosion after tempering and a forced polishing of the parts.

 

Availability

Coils: cold drawn and polished, 10-35kg/coil

Bars: 0-1.99 mm: cold drawn and polished

Bars: 2.00-40mm: cold drawn, ground and polished

Bars length: 2m or 3m surface roughness N5-N6

 

Standard Tolerances

Diameter: ISO h8 ( 3-10mm h7)

Length of bars: +/- 30mm

Out of Roundness/eccentricity: 1/2 of diameter

 

Heat Treatment

Soft annealing: 750-800C slow furnace cooling (2-4 hours)

Hardening: 1000-1050 C

Max obtainable hardness 55 HRC

 

Cutting Rate

40-55 m/min (approximate value, depending on the lubrication, the cutting tools, the shape of parts)

 