Hardenable, Unalloyed free-cutting steel

Chemical Composition Limits

Weight %  C Si Mn P Pb S Fe
LABOR Pb  0.65-0.75 0.10-0.40  0.50-0.90  0.07 Max  0.15-0.30 0.15-0.30 Rem 

Other Chemically similar Specifications 

Weight %  C Si Mn P Pb S Fe
WS 1.0759  0.65-0.75 0.10-0.40   0.50-0.90  0.07 Max  0.15-0.30 0.15-0.30 Rem 
DIN 70 SPb 20  0.65-0.75 0.10-0.40   0.50-0.90  0.07 Max  0.15-0.30 0.15-0.30 Rem 

LABOR Pb material is Manufactured in Rod, Bar and coil

WS 1.0759 Steel - Free Cutting - Unalloyed

 

Stock Range 

Range from 0.80 to 12.50mm

Diameters

3.00mm drawn decarb free and polished

3.00mm drawn decarb free, ground and polished, surface Ra 0.40

 

Mechanical Properties

Tensile Strength at delivery from 650 to 900 N/mm2

 

Availability

Available in 3 or 2 mtr bars or in coil for Escomatic machines

 

Heat Treatment

810-830C hardening in oil for <5mm

790-810C hardening in oil for <5mm

660-700C soft annealing

 

Max obtainable hardness

63-65 HRC 9 for parts with high hardness.

 

Cutting Rate

60 to 80m/min dependant on lubrication oil, the cutting tool and the shape of the parts

 

Tolerance

h8, more accurate tolerances available on request.

 