CDA 101

COPPER 101 NOMINAL DATA SHEET
CHEMICAL COMPOSITION: 99.99% CU min./.0003 PH
ASTM ALLOY NO.: B152
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.322
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C):226
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******) from 68 F to 572 F
(20 C to 300 C):9.8
 

 

COPPER 101 

TENSILE STRENGTH

YIELD STRENGTH(0.2% offset)
(x 1000 PSI (MPA = KSI x 6.8948)
annealed: 26 - 38 8 - 14
1/2 hard: 37 - 46 30 - 44
full hard: 43 - 52 41 - 50
spring: 50 - 58 48 - 57
 

Top of Page

ELONGATION % in 2 inches(= % in 50mm)

annealed: 20 - 50
1/2 hard: 8 - 32
full hard: 3 - 16
spring: 2 - 4
 

 

ROCKWELL B HARDNESS
(.020 gauge and over (Rockwell F or 30 T where noted)

annealed:
1/2 hard: 77 - 89(F)
full hard: 86 - 93(F)
spring: 91 - 97(F)
 

Top of Page

CDA 102

 

NOMINAL DATA SHEET
CHEMICAL COMPOSITION: 99.95 CU min./.015-.040 P
ASTM ALLOY NO.: B152
SAE ALLOY NO.: CA122
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.323
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C):196
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******) from 68 F to 572 F
(20 C to 300 C):9.8
 

Top of Page

TENSILE STRENGTH
YIELD STRENGTH(0.2% offset)
(x 1000 PSI (MPA = KSI x 6.8948)
annealed: 26 - 38 8 - 14
1/2 hard: 37 - 46 30 - 44
full hard: 43 - 52 41 - 50
spring: 50 - 58 48 - 57
 

 

ELONGATION % in 2 inches(= % in 50mm)

annealed: 20 - 50
1/2 hard: 8 - 32
full hard: 3 - 16
spring: 2 - 4
 

 

ROCKWELL B HARDNESS
(.020 gauge and over (Rockwell F or 30 T where noted)

annealed:
1/2 hard: 77 - 89(F)
full hard: 86 - 93(F)
spring: 91 - 97(F)
 

Top of Page

CDA 110

 

NOMINAL DATA SHEET
CHEMICAL COMPOSITION: ETP COPPER 99.90 CU min./.05 OXYGEN Max.
ASTM ALLOY NO.: B152
SAE ALLOY NO.: CA110
FEDERAL SPECS.: QQC576
DENSITY(lbs. per cu. in at 68 F (Annealed) (x 27.68 = gms/cu cm at 20 C):.322
MOD. OF ELAST.(x 10****** PSI, tension):17
ELECT. COND.(% IACS at 68 F (20 C) as annealed):101
THERM. COND.
(BTU per sq.ft.per ft.per hr.per F at 68 F,(20 C):226
COEFF.OF TH.EXPN. (Inches/inch/ F x 10(-******) from 68 F to 572 F
(20 C to 300 C):9.8
 

Top of Page

TENSILE STRENGTH
YIELD STRENGTH(0.2% offset)
(x 1000 PSI (MPA = KSI x 6.8948)
annealed: 26 - 38 8 - 14
1/2 hard: 37 - 46 30 - 44
full hard: 43 - 52 41 - 50
spring: 50 - 58 48 - 57
 

 

ELONGATION % in 2 inches(= % in 50mm)

annealed: 20 - 50
1/2 hard: 8 - 32
full hard: 3 - 16
spring: 2 - 4
 

 

ROCKWELL B HARDNESS
(.020 gauge and over(Rockwell F or 30 T where noted)

annealed:
1/2 hard: 77 - 89(F)
full hard: 86 - 93(F)
spring: 91 - 97(F)
 

Top of Page

CDA 101, CDA 102, ETP Copper 110
COPPER ALLOYS 101/102/110

COIL and FOIL

.003
.004
.005
.010
.015
.020
.032
.040
.050
.062


*NOTE: Other sizes available upon request.

Top of Page